Exclusive agent for foreign insulating material brands
Product Overview
Japan Toyo Vulcanized Fiberboard uses natural materials and is made of base paper from cotton pulp and refined wood pulp. After the base paper is immersed in a zinc chloride solution and the base paper is laminated to a desired thickness, the residual zinc chloride solution is sufficiently removed by a water washing method, and the vulcanized fiberboard is formed by a drying process.
Basic performance
Toyo vulcanized fiberboard is made of natural materials. With the following diverse features:
‧Good mechanical properties
‧ impact resistance, wear resistance, compression resistance, good toughness
‧Lightweight, oil resistant, chemical resistant
‧Not hot, no condensation, absorption/release of moisture
‧Biodegradable and antistatic properties
Product specifications
Product Overview
Japan Toyo Vulcanized Fiberboard uses natural materials and is made of base paper from cotton pulp and refined wood pulp. After the base paper is immersed in a zinc chloride solution and the base paper is laminated to a desired thickness, the residual zinc chloride solution is sufficiently removed by a water washing method, and the vulcanized fiberboard is formed by a drying process.
Basic performance
Toyo vulcanized fiberboard is made of natural materials. With the following diverse features:
‧Good mechanical properties
‧ impact resistance, wear resistance, compression resistance, good toughness
‧Lightweight, oil resistant, chemical resistant
‧Not hot, no condensation, absorption/release of moisture
‧Biodegradable and antistatic properties
Product specifications
Items | P-861 |
Thickness (mm). | 0.5-2.36 |
Density(g/cm3) density | 1.10-1.40 |
Tensile Strength(Mpa) Length | 80-120 |
Tensile Strength (Mpa) Width | 45-80 |
Elongation(%) Length | 1-13 |
Elongation(%) Width | 2-15 |
Bending Strength | No anomalies |
Min Dielectric Strength | 15-30 |
Pared session(N/m ) Y type | -- |
Shrinkage(%) Length | 0.5-2.0 |
Shrinkage(%) Width | 1.0-3.0 |
Shrinkage(%) Thickness | 2.0-6.0 |
Moisture | 6.0-10.0 |
Chlorine content | <0.05 |
Water absorption (1H%) | <10 |
Maximum temperature for usual use(°C). | 120 |
Temp index heat resistance rating | And |
UL 94 flame test | 94-HB |
Applications
Toyo vulcanized fiberboard is made from selected cotton pulp and wood pulp. It is a green and environmentally friendly product. It can be returned to nature through microbial decomposition. As a non-hazardous, environmentally friendly vulcanized fiberboard, it is widely used for its excellent properties:
‧Weak electricity, heavy equipment parts
‧Mechanical parts
‧Material for grinding products
‧Construction materials such as containers and bags
‧Stationery, hooking tools, cutting tools, etc.
Applications
Toyo vulcanized fiberboard is made from selected cotton pulp and wood pulp. It is a green and environmentally friendly product. It can be returned to nature through microbial decomposition. As a non-hazardous, environmentally friendly vulcanized fiberboard, it is widely used for its excellent properties:
‧Weak electricity, heavy equipment parts
‧Mechanical parts
‧Material for grinding products
‧Construction materials such as containers and bags
‧Stationery,
hooking tools, cutting tools, etc.